Why there is a shortage of underinjection during the process

After any special situation occurs during the processing of the dual color injection mold, we need to analyze the root cause of the special situation in order to find the appropriate strategy to solve it. After the summary of experienced engineers, the following are some of the reasons for underinjection.

The main reason for the occurrence of underflow is that the flow resistance of the molten plastic is too high, causing the melt to be unable to continue flowing. The flow factors affecting molten plastic include: wall thickness of plastic parts, temperature of plastic injection molds, pressure during injection molding, temperature of molten plastic, and plastic material composition. These factors may all lead to the occurrence of underinjection. Why does underinjection occur during injection

After any special situation occurs during the processing of the dual color injection mold, we need to analyze the root cause of the special situation in order to find the appropriate strategy to solve it. After the summary of experienced engineers, the following are some of the reasons for underinjection.

The main reason for the occurrence of underflow is that the flow resistance of the molten plastic is too high, causing the melt to be unable to continue flowing. The flow factors affecting molten plastic include: wall thickness of plastic parts, temperature of plastic injection molds, pressure during injection molding, temperature of molten plastic, and plastic material composition. These factors may all lead to the occurrence of underinjection. Why does underinjection occur during injection